High-yield carbon derived from commercial phenol–formaldehyde resin for broadband microwave absorption by balancing conductivity and polarization loss. / Shi, Y; Li, X; Liu, Qiuyun et al.
Yn: Journal of Materials Science, Cyfrol 58, 04.2023, t. 7048-7059.

Allbwn ymchwil: Cyfraniad at gyfnodolynErthygladolygiad gan gymheiriaid

HarvardHarvard

APA

CBE

MLA

VancouverVancouver

Shi Y, Li X, Liu Q, Zhang C, Guo W, Tian K et al. High-yield carbon derived from commercial phenol–formaldehyde resin for broadband microwave absorption by balancing conductivity and polarization loss. Journal of Materials Science. 2023 Ebr;58:7048-7059. Epub 2023 Ebr 19. doi: 10.1007/s10853-023-08465-9

Author

RIS

TY - JOUR

T1 - High-yield carbon derived from commercial phenol–formaldehyde resin for broadband microwave absorption by balancing conductivity and polarization loss

AU - Shi, Y

AU - Li, X

AU - Liu, Qiuyun

AU - Zhang, C

AU - Guo, W

AU - Tian, K

AU - Elias, Rob

AU - Wang, H

PY - 2023/4

Y1 - 2023/4

N2 - Lightweight and chemically stable carbon are widely applied as attractive microwave absorption materials (MAMs). However, the effective response bandwidth of pure carbonaceous MAMs is limited due to the imbalance between conductivity and polarization loss. Herein, carbon with a large number of amorphous/nanocrystalline uneven phase interfaces prepared from commercial phenol–formaldehyde resin (PF) through simple anoxic carbonization exhibited excellent microwave absorption performance by balancing conductivity and polarization loss. Benefiting from the modification of the carbon nanocrystalline, a suitable electrical conductivity is obtained with a large number of amorphous/nanocrystalline uneven phase interfaces, allowing more incident microwaves to be lost. Thus, PF-650 exhibits a strong reflection loss of − 59.62 dB and a broadband effective microwave absorption of 6.32 GHz at 2.35 mm. In contrast to typical carbonaceous MAMs with multiple chemical compositions and complicated microstructures, this work provides a promising approach to the preparation of highly efficient and yielding carbonaceous materials for practical applications.

AB - Lightweight and chemically stable carbon are widely applied as attractive microwave absorption materials (MAMs). However, the effective response bandwidth of pure carbonaceous MAMs is limited due to the imbalance between conductivity and polarization loss. Herein, carbon with a large number of amorphous/nanocrystalline uneven phase interfaces prepared from commercial phenol–formaldehyde resin (PF) through simple anoxic carbonization exhibited excellent microwave absorption performance by balancing conductivity and polarization loss. Benefiting from the modification of the carbon nanocrystalline, a suitable electrical conductivity is obtained with a large number of amorphous/nanocrystalline uneven phase interfaces, allowing more incident microwaves to be lost. Thus, PF-650 exhibits a strong reflection loss of − 59.62 dB and a broadband effective microwave absorption of 6.32 GHz at 2.35 mm. In contrast to typical carbonaceous MAMs with multiple chemical compositions and complicated microstructures, this work provides a promising approach to the preparation of highly efficient and yielding carbonaceous materials for practical applications.

U2 - 10.1007/s10853-023-08465-9

DO - 10.1007/s10853-023-08465-9

M3 - Article

VL - 58

SP - 7048

EP - 7059

JO - Journal of Materials Science

JF - Journal of Materials Science

SN - 0022-2461

ER -